|本期目录/Table of Contents|

[1]李建军,甘玉花,王伟明,等.碱处理法改性ZSM5分子筛催化苯与乙醇烷基化制乙苯[J].厦门大学学报(自然科学版),2012,51(5):882.
 LI Jian jun,GAN Yu hua,WANG Wei ming,et al.Study on Surface Acidity and Morphology of Alkalinetreated ZSM5Zeolite for Alkylation of Benzene with Ethanol to Ethylbenzene[J].Journal of Xiamen University(Natural Science),2012,51(5):882.
点击复制

碱处理法改性ZSM5分子筛催化苯与乙醇烷基化制乙苯(PDF)
分享到:

《厦门大学学报(自然科学版)》[ISSN:0438-0479/CN:35-1070/N]

卷:
51卷
期数:
2012年第5期
页码:
882
栏目:
研究论文
出版日期:
2012-09-20

文章信息/Info

Title:
Study on Surface Acidity and Morphology of Alkalinetreated ZSM5 Zeolite for Alkylation of Benzene with Ethanol to Ethylbenzene
作者:
李建军1甘玉花1王伟明1方维平12杨意泉12*
1.厦门大学化学化工学院,2.厦门大学醇醚酯清洁生产国家工程实验室,福建 厦门 361005
Author(s):
LI Jianjun1GAN Yuhua1WANG Weiming1FANG Weiping1YANG Yiquan12*
1.College of Chemistry and Chemical Engineering,Xiamen University,2.National Engineering Laboratory for Green Chemical Products of AlcoholsEthersEsters,Xiamen University,Xiamen 361005,China
关键词:
ZSM5分子筛碱处理烷基化
Keywords:
ZSM5 zeolitealkalitreatmentalkylationbenzene
分类号:
O 643.3
文献标志码:
-
摘要:
用不同浓度的NaOH溶液对ZSM5分子筛进行改性,以XRD、SEM、NH3TPD和BET方法对改性前后的催化剂进行表征,并考察了碱处理改性对ZSM5分子筛孔结构、酸性以及催化苯与乙醇烷基化反应的性能的影响.结果表明,通过调变NaOH溶液浓度可以在保持ZSM5分子筛的微孔骨架结构的同时,调变介孔分布.随着NaOH溶液浓度升高,ZSM5分子筛的酸量、介孔孔容、介孔表面积都增加,孔径分布变宽,从而改善了催化剂的催化性能.对ZSM5分子筛进行碱改性,比较合适的NaOH溶液浓度为0.2 mol/L,改性后的ZSM5分子筛催化剂具有较高的活性和稳定性.但超过0.5 mol/L的NaOH溶液会破坏ZSM5分子筛骨架结构,该浓度的NaOH溶液改性后的ZSM5分子筛催化活性下降较快.
Abstract:
The alkylation of benzene with ethanol to produce ethylbenzene over ZSM5 catalyst has been widely investigated.In order to improve the ZSM5 catalyst performance,the ZSM5 zeolite catalysts were modified by desilication treatment in alkaline solution with different concentrations for the alkylation of benzene with ethanol to ethylbenzene,and characterized by Xray diffraction (XRD),scanning electron microscope(SEM),NH3TPD,and BET techniques.The characterization results show that mesopore size distribution of the catalysts can be controlled by changing NaOH solution concentration without destroying framework of ZSM5 zeolite.With the increase concentration of NaOH solution,the amount of acid sites,mesopore volume,and specific surface area increased,the pore size distribution became broader.Therefore,the catalytic performance for the reaction was effectively improved.It was found that the optimal concentration of NaOH solution used to treat the ZSM5 zeolite was 0.2 mol/L.When the NaOH concentration was over 0.5 mol/L the framework of ZSM5 zeolite was found to be severely destroyed.

参考文献/References:


[1]赵仁殿.芳烃工学[M].北京:化学工业出版社,1994:234.
[2]朱晓茹.改性纳米HZSM5催化剂上生物乙醇脱水制乙烯的研究[D].大连:大连理工大学,2007.
[3]徐海升,王安中.在ZSM5分子筛催化剂上苯与乙醇合成乙苯的研究[J].化学工程,1989,17(2):118119.
[4]魏辉荣,王留成,徐海升.磷镁改性ZSM5分子筛催化剂上苯与乙醇合成乙苯的研究[J].郑州工学院学报,1992, 13(2):6065.
[5]Yuan Junjun,Borje S G.Alkylation of benzene with ethanol over ZSM5 catalyst with different SiO2/Al2O3 ratios [J].Indian J Chem Technol,2004,11:337345.
[6]Vijayaranghavan V R,Joseph K,Raj A.Ethylation of benzene with ethanol over substituted large pore aluminophosphatebased molecular sieves [J].J Mol Catal A:Chem,2004(207):4150.
[7]高俊华,张立东,胡津仙,等.不同HZSM5催化剂上苯与乙醇的烷基化反应[J].石油学报,2009,25(1):6065.
[8]PérezRamírez J,Kapteijn F,Groen J C,et al.Steamactivated FeMFI zeolites.Evolution of iron species and activity in direct N2O decomposition [J].J Catal,2003,214 (1):3345.
[9]Corma A.From microporous to mesoporous molecular sieve materials and their use in catalysis [J].Chem Rev,1997,97(6):23732420.
[10]Zhang Cunman,Liu Qian,Xu Zheng,et al.Synthesis and characterization of composite molecular sieves with mesoporous and microporous structure from ZSM5 zeolites by heat treatment [J].Microporous Mesoporous Material,2003,62:157163.
[11]Cartlidge S,Nissen H U,Wessicken R.Ternary mesoporous structure of ultra stable zeolites CSZ1[J].Zeolites,1989,9(4):346351.
[12]Kortunov P,Vasenkov S,Karger J,et al.The role of mesoporous in intracrystalline transport in USY zeolite:PFG NMR diffusion study on various length scales [J].J Am Chem Soc,2005,127(37):1305513059.
[13]Suzuki T,Okuhar T.Change in pore structure of MFI zeolite by treatment with NaOH aqueous solution[J].Microporous Mesoporous Mater,2001,43(1):8389.
[14]Ogura M,Shunomiya S,Tateno J,et al.Alkalitreatment techniquenew method for modification of structure and acidcatalytic properties of ZSM5 zeolites[J].Applied Catalysis A,2001,219(1/2):3343.
[15]Groen J C,Peffer L A A,Moulijn J A,et al.Mesoporosity development in ZSM5 zeolite upon optimized desilication conditions in alkaline medium[J].Colloids Surf A:Physicochem Eng,2004,214:5358.
[16]Groen J C,Zhu Weidong,Brouwer S,et al.Direct demonstration of enhanced diffusion in mesoporous ZSM5 zeolite obtained via controlled desilication[J].J Am Chem Soc,2007,129(2):355360.
[17]Katoh M,Yoshikawa T,Tomonari T,et al.Adsorption characteristics of ionexchanged ZSM5 zeolites for CO2/N2 mixtures [J].J Colloid Interface Sci,2000,226:145150.
[18]Abello S,Bonilla A,Ramirez J P.Mesoporous ZSM5 zeolite catalysts prepared by desilication with organic hydroxides and comparison with NaOH leaching[J].Applied Catalysis A:General,2009,364:191198.
[19]金文清,赵国良,滕加伟,等.氢氧化钠改性ZSM5分子筛的碳四烯烃催化裂化性能[J].化学反应工程与工艺,2007,23(3):193199.
[20]Song Y Q,Zhu X X,Yi S,et al.An effect method to enhance the stability onstream of butene aromatization:posttreatment of ZSM5 by alkali solution hydroxide[J].Applied Catalysis A,2006,302(1):6977.
[21]蒋培兴,李全芝.程序升温脱附法研究HZMS5和HM分子筛的酸性质[J].催化学报,1983,4(3):232240.
[22]严贻春,谢常实,秦关林.氨在HZSM5沸石上的吸附与程序升温脱附[J].催化学报,1984,5(1):8790.
[23]张怀彬,潘履让,李赫喧.HZSM5的表面B酸与催化活性[J].燃料化学报,1991,19(1):813.
[24]Tao Yousheng,Kanoh H,Abrams,et al.Mesoporemodified zeolites:preparation,characterization,and applications [J].Chem Rev,2006,106:896910.
[25]吴伟,李凌飞,武光,等.碱脱硅改性的ZSM12分子筛择形催化合成2,6二甲基萘的研究[J].现代化工,2009,29(6):4045.
[26]祁晓岚,陈雪梅,孔德金,等.介孔丝光沸石的制备及其对重芳烃转化反应的催化性能[J].催化学报,2009,30(12):11971202.
[27]Csicsery S M.Shapeselective catalysis in zeolites [J].Zeolites,1984,4:202213.
[28]潘履让,郝玉芝,李赫喧.苯与乙醇烷基化制乙苯的研究:III.HZSM5及其改性后的酸性和催化性能[J].燃料化学学报,1988,16(3):199204.

备注/Memo

备注/Memo:
收稿日期:20120424*通信作者:yyiquan@xmu.edu.cn
更新日期/Last Update: 2012-09-20